UNI PLAST (APP)


[Contact us for a price]

In stock

1.    

UNIPLAST APP 4604

                                                                                 

DESCRIPTION

   Is the new generation polymer modified bituminous waterproofing membrane, consisting of a central non woven polyester core, impregnated and coated on both sides with layers of APP (A tactic  Polypropylene Polymer) modified bitumen and finished with heat fusible Polyethylene film on both surfaces.

properties

Specification

Test Method

Roll size (L x W).m

10x1

10x1

10x1

UEAtc,M.O.A.T.30

Thickness, mm

4

4

4

UEAtc,M.O.A.T.30

Unit weight ,kg/m2

4.5

4.5

4.5

UEAtc,M.O.A.T.30

Carrier (polyester) weight ,g/m2

160(Green)

180(Green)

200(Green)

UEAtc,M.O.A.T.30

Coating Asphalt Type

Softening Point (R&B),oC

 Penetration at 25 oC, 0.1mm

Modified Asphalt >140o C

 15-25

Modified Asphalt

>140o C

25-35

Modified Asphalt >140o C

25-35

 

ASTM D 36

ASTM D 5

Tensile Strength N/5 cm

             Longitudinal

             Transversal

 

650

500

 

850

700

 

950

750

 

UEAtc,M.O.A.T.30

Elongation at Break, %

             Longitudinal

             Transversal  

 

45

50

 

45

50

 

45

50

 

UEAtc,M.O.A.T.30

Tear Resistance

              Longitudinal

              Transversal

 

250

275

 

350

300

 

450

325

 

ASTM D 5147

Lap Joint Strength, N/5 cm

              Longitudinal

              Transversal

 

550

425

 

750

650

 

850

700

 

UEAtc,M.O.A.T.30

Cold Flexibility at (0 to-5 oC)

No Cracking

No Cracking

No Cracking

      ASTM D 5147

Heat Resistance at 110oC

No Flowing

No Flowing

No Flowing

      ASTM D 5147

Resistance to water pressure 2 bars(0.2Mpa)

No leakage

No leakage

No leakage

      DIN 52123

Water Absorption, %(BSP)

0.1

0.1

0.1

      ASTM D 5147

 

 

 

 

UNIPLAST, APP 4604 is the Ultimate Waterproofing Membrane. The multilayered design consist of non woven polyester core, impregnated and coated on both sides with APP              ( A tactic   Polypropylene Polymer) modified bitumen and finally finished with fusible polyethylene film on both surfaces.APP 4604 modified bituminous waterproofing membrane are product from a blend of special grade thermoplastic polymers and bitumen. This combination gives the proven waterproofing qualities of bitumen plasticity, excellent resistance to heat, ageing   and weathering and ease of application by torch welding. The polyester core gives the membrane high tensile strength, elongation and superior lap joint strength.

UNIPLAST is available with two finishes

1-with polyethylene film both side (UNIPLAST-S)

2- with polyethylene film one side and granular for the other side (UNIELAST-G).

UNIPLAST is available (4mm , 3mm)

Features:

Ø  Total Impermeability for complete waterproofing.

Ø  Good bond ability and seam integrity.

Ø  Stability at high ambient temperature.

Ø  Good performance at broad temperature range.

Ø  Good flexibility.

Ø  Compatible with all roofing and building component.

UNIPLAST it could be widely used in all kinds of waterproof engineering project in all fields,

Especially for the following types of engineering projects:

Ø  All kinds of building roof engineering projects, treading, non-treading, planting building surfaces.

Ø  All kinds of underground waterproof of damp roof engineering projects.

Ø  Water spraying pools, swimming pools, penstocks, water pools and similar works.

Surface Preparation:

Ø  Clean the surface smooth and free of moisture and debris or any kind of substance that would prevent the membrane from adhering properly.

Ø  The roof must have a minimum slope of 1 %( 10mm per meter) evenly and continuously towards the drains.

Ø  Surface must be primed with UIB Primer D41 or any other primers under ASTM 41.

 

Membrane Installation:

Ø  Unroll the membrane. Making sure that the edge (side lap joint) is aligned with the low point of the roof. Re-roll one end to the centre of the roll and apply; then proceed with the opposite half. Proceed up the slope with further rolls.

Ø  The end of the propane torch head should be positioned between 150mm and 300mm from surfaces, depending on the weather conditions. Maximum heat is obtained at the blue end of the flame. The welding procedure will be more if the torch and thus the flame are moved continuously in a rectangular pattern from the roll to the substrate. The movement should be slowed over the joint of the base sheet in order to apply enough heat to soften the bitumen   and to fill possible voids.

Ø  For best results, make sure that there is always a small amount of molten bitumen in front of the roll being heat welded. When in doubt, re-roll and strings of bitumen should appear between the roll and the substrate.

Packing:

UNIPLAST 23 Roll per pallet.

Storage and Handling:

Ø  Vertically stored the rolls in pallets.

Ø  Store under shaded warehouse.

Ø  Rolls in pallet should not be stored over the other.

Manufacturer’s Warranty:

Subject to conditions and limitations of UIBF (Union International bitumen factory Co.) may modify the composition and/or utilization of its products without prior notice consequently orders will be filled according to the latest specifications.